Investigation of Dimethylammonium Solubility in MAPbBr3 Hybrid Perovskite: Synthesis, Crystal Structure, and Optical Properties
Inorganic Chemistry ( IF 4.3 ) Pub Date : 2018-12-14 00:00:00 , DOI: 10.1021/acs.inorgchem.8b03072 Camilla Anelli 1 , Michele R. Chierotti 2 , Simone Bordignon 2 , Paolo Quadrelli 1 , Daniela Marongiu 3 , Giovanni Bongiovanni 3 , Lorenzo Malavasi 1
Inorganic Chemistry ( IF 4.3 ) Pub Date : 2018-12-14 00:00:00 , DOI: 10.1021/acs.inorgchem.8b03072 Camilla Anelli 1 , Michele R. Chierotti 2 , Simone Bordignon 2 , Paolo Quadrelli 1 , Daniela Marongiu 3 , Giovanni Bongiovanni 3 , Lorenzo Malavasi 1
Affiliation
|
The possible existence of mixed methylammonium (MA)/dimethylammonium (DMA) lead bromide hybrid perovskites of general formula MA1–xDMAxPbBr3 (0 ≤ x ≤ 1) was investigated. A combined X-ray diffraction and solid-state nuclear magnetic resonance approach indicates that DMA can be incorporated up to about x = 0.30 while retaining the cubic lattice of MAPbBr3. By increasing the DMA content (x), the absorption shows a progressive blue shift and the band gap moves from about 2.17 eV (x = 0) to about 2.23 (x = 0.30) with a concomitant slightly faster recombination in the mixed cation powders.
中文翻译：
二甲基铵在MAPbBr 3杂化钙钛矿中的溶解度研究：合成，晶体结构和光学性质
混合甲基铵（MA）/二甲基铵（DMA）通式MA的溴化铅混合钙钛矿可能存在的1- X DMA X PbBr 3（0≤ X ≤1）进行了调查。X射线衍射和固态核磁共振相结合的方法表明，在保留MAPbBr 3的立方晶格的同时，DMA的掺入量最高可达x = 0.30 。通过增加DMA含量（x），吸收显示出渐进的蓝移，并且带隙从约2.17 eV（x = 0）移至约2.23（x = 0.30），同时在混合阳离子粉末中的复合速度稍快。
更新日期：2018-12-14
中文翻译：
二甲基铵在MAPbBr 3杂化钙钛矿中的溶解度研究：合成，晶体结构和光学性质
混合甲基铵（MA）/二甲基铵（DMA）通式MA的溴化铅混合钙钛矿可能存在的1- X DMA X PbBr 3（0≤ X ≤1）进行了调查。X射线衍射和固态核磁共振相结合的方法表明，在保留MAPbBr 3的立方晶格的同时，DMA的掺入量最高可达x = 0.30 。通过增加DMA含量（x），吸收显示出渐进的蓝移，并且带隙从约2.17 eV（x = 0）移至约2.23（x = 0.30），同时在混合阳离子粉末中的复合速度稍快。