MOF-Derived Porous Co3O4 Hollow Tetrahedra with Excellent Performance as Anode Materials for Lithium-Ion Batteries
Inorganic Chemistry ( IF 4.3 ) Pub Date : 2015-08-11 00:00:00 , DOI: 10.1021/acs.inorgchem.5b00544
Dan Tian 1 , Xian-Long Zhou 1 , Ying-Hui Zhang 1 , Zhen Zhou 1 , Xian-He Bu 1
Inorganic Chemistry ( IF 4.3 ) Pub Date : 2015-08-11 00:00:00 , DOI: 10.1021/acs.inorgchem.5b00544
Dan Tian 1 , Xian-Long Zhou 1 , Ying-Hui Zhang 1 , Zhen Zhou 1 , Xian-He Bu 1
Affiliation
|
Porous Co3O4 hollow tetrahedra were prepared through the thermolysis of metal–organic frameworks and presented reversible capacities of 1196 and 1052 mAh g–1 at 50 and 200 mA g–1 after 60 charge/discharge cycles, respectively. Such excellent performances stem from the well-defined hollow structure of Co3O4 tetrahedra.
中文翻译：
MOF衍生的多孔Co 3 O 4空心四面体，具有优异的性能，可作为锂离子电池的负极材料
多孔的Co 3 O 4中空四面体是通过金属-有机骨架的热解制备的，在60个充放电循环后，分别在50和200 mA g -1时可逆容量分别为1196和1052 mAh g –1。如此出色的性能源于Co 3 O 4四面体的明确定义的空心结构。