A series of Nd³⁺/Yb³⁺ co-doped Ca₂LaTaO₆ (CLTO) phosphors are synthesized by a high temperature solid phase method. Structural characterization confirms the successful incorporation of Nd³⁺ and Yb³⁺ ions into the CLTO host lattice. The photoluminescence excitation (PLE) spectra and photoluminescence (PL) spectra of CLTO:Nd³⁺ and CLTO:Nd³⁺/Yb³⁺ are investigated in detail. Under the excitation of ultraviolet (UV) and visible (VIS) light, the CLTO:Nd³⁺/Yb³⁺ phosphor emits broadband near infrared (NIR) luminescence. In particular, the luminescence intensity of the Yb³⁺ ion is increased through an energy transfer (ET) process from Nd³⁺ to Yb³⁺. The luminescence mechanism of the CLTO:Nd³⁺/Yb³⁺ sample is analyzed based on the decay lifetime and PL spectra. In addition, the NIR emission intensity of Yb³⁺ ions is also enhanced by doping K⁺ ions. The broadband luminescence (850–1050 nm) of the CLTO:Nd³⁺/Yb³⁺/K⁺ phosphor has good application in solar cells and anti-counterfeiting.

中文翻译：

---

Ca2LaTaO6：Nd3+/Yb3+/K+荧光粉的近红外下移发光及其应用：太阳能电池和防伪


通过高温固相法合成了一系列 Nd³⁺/Yb³⁺ 共掺杂的 Ca₂LaTaO₆ （CLTO） 荧光粉。结构表征证实了 Nd³⁺ 和 Yb³⁺ 离子成功掺入 CLTO 主晶格中。详细研究了 CLTO：Nd³⁺ 和 CLTO：Nd³⁺/Yb³⁺ 的光致发光激发 （PLE） 光谱和光致发光 （PL） 光谱。在紫外光 （UV） 和可见光 （VIS） 的激发下，CLTO：Nd³⁺/Yb³⁺ 荧光粉发出宽带近红外 （NIR） 发光。特别是，Yb³⁺ 离子的发光强度通过能量转移 （ET） 过程从 Nd³⁺ 增加到 Yb³⁺。根据衰变寿命和 PL 光谱分析 CLTO：Nd³⁺/Yb³⁺ 样品的发光机理。此外，掺杂 K⁺ 离子也增强了 Yb³⁺ 离子的 NIR 发射强度。CLTO：Nd³⁺/Yb³⁺/K⁺ 荧光粉的宽带发光 （850–1050 nm） 在太阳能电池和防伪方面具有良好的应用。