Reduction of non‐radiative energy loss (ΔEnr) in all‐polymer solar cells (all‐PSCs) is crucially important for achieving high power conversion efficiencies (PCEs). Herein, an efficient strategy is reported to reduce the ΔEnr by introducing luminescent unit into the backbone of polymer acceptors. Compared to the device based on PM6:PYDT, the ΔEnr in all‐PSC based on PM6:PYDT‐CzP‐9 has decreased from 0.188 to 0.183 eV. This reduction is attributed to the improvement in electroluminescence external quantum efficiency (EQEEL). The PM6:PYDT‐CzP‐9 device has shown an 18% increase in EQEEL compared to the device based on PM6:PYDT (8.4 × 10−4 vs 7.1 × 10−4), demonstrating that the incorporation of luminescent unit in polymer acceptors is highly effective in enhancing the electroluminescence performance of all‐PSCs. As a result, the PM6:PYDT‐CzP‐9 device yielded a high VOC of 0.967 V, without the sacrifice of short‐circuit current density (23.42 mA cm−2) and fill factor (77.5%), leading to a high PCE of 17.55%.

中文翻译：

---

聚合物受体与发光单元共聚，用于具有低非辐射能量损失的高性能全聚合物太阳能电池


减少全聚合物太阳能电池 （all-PSC） 中的非辐射能量损失 （ΔEnr） 对于实现高功率转换效率 （PCE） 至关重要。在此，报道了一种通过将发光单元引入聚合物受体的主链来降低 ΔEnr 的有效策略。与基于 PM6：PYDT 的设备相比，基于 PM6：PYDT-CzP-9 的全 PSC 中的 ΔEnr 从 0.188 eV 降低到 0.183 eV。这种降低归因于电致发光外部量子效率 （EQEEL） 的提高。与基于 PM6：PYDT 的设备相比，PM6：PYDT-CzP-9 设备的 EQEEL 增加了 18%（8.4 × 10-4 对 7.1 × 10-4），表明在聚合物受体中掺入发光单元在增强全 PSC 的电致发光性能方面非常有效。结果，PM6：PYDT-CzP-9 器件产生了 0.967 V 的高 VOC，而没有牺牲短路电流密度 （23.42 mA cm-2） 和填充因子 （77.5%），导致 17.55% 的高 PCE。