Revealing and Inhibiting the Facet-related Ion Migration for Efficient and Stable Perovskite Solar Cells
Angewandte Chemie International Edition ( IF 16.1 ) Pub Date : 2024-09-17 , DOI: 10.1002/anie.202415949 Shujie Qu 1 , Hao Huang 1 , Jinhui Wang 1 , Peng Cui 1 , Yiyi Li 2 , Min Wang 1 , Liang Li 1 , Fu Yang 1 , Changxu Sun 1 , Qiang Zhang 1 , Pengkun Zhu 1 , Yi Wang 2 , Meicheng Li 3
Angewandte Chemie International Edition ( IF 16.1 ) Pub Date : 2024-09-17 , DOI: 10.1002/anie.202415949 Shujie Qu 1 , Hao Huang 1 , Jinhui Wang 1 , Peng Cui 1 , Yiyi Li 2 , Min Wang 1 , Liang Li 1 , Fu Yang 1 , Changxu Sun 1 , Qiang Zhang 1 , Pengkun Zhu 1 , Yi Wang 2 , Meicheng Li 3
Affiliation
|
We first reveal the unknown relation between ion migration and crystal facet, in which the (100) facet is substantially more vulnerable to occur cationic migration than the (111) facet, and then control the (111)-orientation through an antisolvent strategy. The PSCs with (111)-dominated perovskite achieve a PCE of 26.0 % (25.4 % certification), and can maintain >95 % of their initial PCEs after 3500-hours operation under 1-sun illumination.
中文翻译：
揭示和抑制与 Facet 相关的离子迁移，实现高效稳定的钙钛矿太阳能电池
我们首先揭示了离子迁移和晶体刻面之间的未知关系，其中 （100） 刻面比 （111） 刻面更容易发生阳离子迁移，然后通过反溶剂策略控制 （111） 取向。具有 （111） 为主的钙钛矿的 PSC 实现了 26.0 % 的 PCE（25.4 % 认证），并且在 1 个太阳光照下运行 3500 小时后，可以保持其初始 PCE 的 >95 %。