2-Aminoanilinium benzene-1, 2-diaminium tris (4-methylbenzene-1-sulfonate) organic single crystal was grown by slow evaporation solution growth technique at ambient temperature. The grown crystal was subjected to single-crystal X-ray diffraction studies to confirm the crystal structure. The presence of different molecular groups and modes of vibrations was identified by FTIR analysis. UV- visible spectral studies revealed the transparency, lower cut-off wavelength, bandgap energy, optical parameters such as refractive index (n), extinction coefficient (k), optical conductivity, and electrical conductivity. Laser-induced damage threshold was calculated as 3.5 GW/cm². Mechanical properties of grown crystal were investigated by Vicker’s micro-hardness test. The dielectric measurement at room temperature showed the electrical behavior of the crystal.

采用缓慢蒸发溶液生长技术在环境温度下生长了2-氨基苯胺苯-1, 2-二胺三(4-甲基苯-1-磺酸盐)有机单晶。对生长的晶体进行单晶 X 射线衍射研究以确认晶体结构。通过 FTIR 分析确定了不同分子基团和振动模式的存在。紫外-可见光谱研究揭示了透明度、下截止波长、带隙能量、折射率 (n)、消光系数 ( k )、光导率和电导率等光学参数。激光诱导损伤阈值经计算为3.5 GW/cm ²。通过维氏显微硬度测试研究了生长晶体的机械性能。室温下的介电测量显示了晶体的电学行为。