氢键相互作用衍生亚微米硅阳极上的均匀石墨烯涂层
Battery Energy ( IF 9.0 ) Pub Date : 2024-02-03 , DOI: 10.1002/bte2.20230068 Liewu Li 1 , Yizhao Yang 1 , Zhencheng Huang 1 , Tao Huang 1 , Weibin Chen 1 , Xiaoyu Gong 1 , Shenghua Ye 1 , Hao Li 2 , Shaoluan Huang 3 , Wei Xiong 3 , Jing Chen 4 , Hongbin Wang 1 , Xiangzhong Ren 1 , Xiaoping Ouyang 4 , Jionghui Wang 5 , Qianling Zhang 1 , Jiangtao Hu 1 , Jianhong Liu 1, 3
Battery Energy ( IF 9.0 ) Pub Date : 2024-02-03 , DOI: 10.1002/bte2.20230068 Liewu Li 1 , Yizhao Yang 1 , Zhencheng Huang 1 , Tao Huang 1 , Weibin Chen 1 , Xiaoyu Gong 1 , Shenghua Ye 1 , Hao Li 2 , Shaoluan Huang 3 , Wei Xiong 3 , Jing Chen 4 , Hongbin Wang 1 , Xiangzhong Ren 1 , Xiaoping Ouyang 4 , Jionghui Wang 5 , Qianling Zhang 1 , Jiangtao Hu 1 , Jianhong Liu 1, 3
Affiliation
|
在追求更高能量密度的锂离子电池（LIB）的过程中，硅（Si）已成为一种有前途的阳极材料。然而，硅阳极的大规模应用受到其显着的膨胀、严重的粉化和连续的电极-电解质反应的阻碍。因此，开发一种有效的方法来减轻硅颗粒膨胀并最大限度地减少界面寄生反应已成为学术界和工业界的一个重要研究热点。在此，报道了一种用于制备双层涂层亚微米硅阳极的简便且可扩展的策略，该阳极包含陶瓷（氧化硅）和石墨烯层，表示为 Si@SiO x @G。在这种方法中，SiO x在Si表面原位合成，并通过氢键相互作用与石墨烯结合。所制备的硅电极表现出优异的结构集成性和出色的电化学稳定性，在1 A g -1下循环540次后容量保持率为92.58% ，并且具有出色的倍率性能，在2 下实现了875 mAh g -1的比容量。 A g -1。这项研究为广泛实施高能量密度硅基电池提供了一种简单而实用的方法。
"点击查看英文标题和摘要"
更新日期：2024-02-04
"点击查看英文标题和摘要"
京公网安备 11010802027423号