Two new indolo[3,2-b]carbazole derivatives containing coumarin fluorophores (2,8-ICZ-C and 3,9-ICZ-C) were synthesized by the introduction of two 7-diethylamino-3-coumarinyl fluorophores at 2,8-positions and 3,9-positions of the indolo[3,2-b]carbazole (ICZ) core, respectively, as the organic emitters for organic light-emitting devices (OLEDs). The photophysical and electrochemical properties and thermal stabilities of the compounds were systematically investigated. These compounds exhibited good thermal stability as well as strong blue emission (Φf of 79.67 % for 2,8-ICZ-C and Φf of 55.90 % for 3,9-ICZ-C) in CH2Cl2 solution. The doped devices with a structure of ITO/PEDOT:PSS (50 nm)/2,6DCzPPy:ICZ derivative (x, wt%) (30 nm)/TPBi (20 nm)/Liq (3 nm)/Al (130 nm) were fabricated by solution-processed the emitting layers, in which the 2,8-ICZ-C device exhibited a maximum luminance (Lmax) of 1425 cd/m2, a maximum current efficiency (CEmax) of 1.24 cd/A and a maximum external quantum efficiency (EQEmax) of 0.71 %, and the 3,9-ICZ-C device showed Lmax, CEmax and EQEmax of 1005 cd/m2, 1.14 cd/A and 0.53 %, respectively.

中文翻译：

---

含香豆素荧光团的吲哚[3,2-b]咔唑衍生物的合成和发光特性


通过在吲哚[3,2-b]咔唑 （ICZ） 核心的 2,8 位和 3,9 位分别引入两个 7-二乙氨基-3-香豆素基荧光团作为有机发光器件 （OLED） 的有机发射器，合成了两种含有香豆素荧光团的新型吲哚[3,2-b]咔唑衍生物（2,8-ICZ-C 和 3,9-ICZ-C）。系统研究了化合物的光物理和电化学性质以及热稳定性。这些化合物在 CH2Cl2 溶液中表现出良好的热稳定性和强烈的蓝色发射（2,8-ICZ-C 的 Φf 为 79.67 %，3,9-ICZ-C 的 Φf 为 55.90 %）。通过对发射层进行固溶处理，制备了结构为 ITO/PEDOT：PSS （50 nm）/2,6DCzPPy：ICZ 衍生物 （x， wt%） （30 nm）/TPBi （20 nm）/Liq （3 nm）/Al （130 nm） 的掺杂器件，其中 2,8-ICZ-C 器件的最大亮度 （Lmax） 为 1425 cd/m2，最大电流效率 （CEmax） 为 1.24 cd/A，最大外部量子效率 （EQEmax） 为 0.71 %， 3,9-ICZ-C 器件的 Lmax、CEmax 和 EQEmax 分别为 1005 cd/m2、1.14 cd/A 和 0.53 %。