通过基于激光的表面改性增强 MAPbBr3 单晶的光致发光
ACS Photonics ( IF 6.5 ) Pub Date : 2023-12-01 , DOI: 10.1021/acsphotonics.3c00777 Ismael Fernandez-Guillen 1 , Vladimir S. Chirvony 1 , Marie Kreĉmarová 1 , Guillermo Muñoz-Matutano 1 , Jesus Ortiga-Fibla 1 , Ana Cros 1 , Núria Garro 1 , Juan F. Sánchez-Royo 1 , Juan P Martínez-Pastor 1 , María Carmen Asensio 1, 2 , Rafael Abargues 1 , Pablo P. Boix 1
ACS Photonics ( IF 6.5 ) Pub Date : 2023-12-01 , DOI: 10.1021/acsphotonics.3c00777 Ismael Fernandez-Guillen 1 , Vladimir S. Chirvony 1 , Marie Kreĉmarová 1 , Guillermo Muñoz-Matutano 1 , Jesus Ortiga-Fibla 1 , Ana Cros 1 , Núria Garro 1 , Juan F. Sánchez-Royo 1 , Juan P Martínez-Pastor 1 , María Carmen Asensio 1, 2 , Rafael Abargues 1 , Pablo P. Boix 1
Affiliation
|
金属卤化物钙钛矿的单晶（SC）有望改善其多晶对应物的良好光电特性，但表面损失代表了非辐射复合形式的重大缺陷。我们表明，蓝色连续激光处理 MAPbBr 3钙钛矿 SC 会导致晶体表面改性，其中包括形成上层 PbBr 2薄膜以及下层晶体钙钛矿，这表明约 75 meV 的扩展带隙。结果，处理后光致发光提高了 2 个数量级。我们认为，在 O 2存在下，激光诱导 CH 3 NH 3 +部分分解后，扩展带隙 MAPbBr 3具有由于拉伸应变而形成的扭曲晶格。甲酸和甲胺作为副产物形成，以钝化变形的 MAPbBr 3层并保护钙钛矿结构免受环境的不利影响，例如水引起的降解。
"点击查看英文标题和摘要"
更新日期：2023-12-01
"点击查看英文标题和摘要"
京公网安备 11010802027423号