外延 LiCoO2 电池阴极的物理脱锂作为表面电子结构研究的平台
ACS Applied Materials & Interfaces ( IF 8.3 ) Pub Date : 2023-07-19 , DOI: 10.1021/acsami.3c06147 Elena Salagre 1 , Pilar Segovia 1, 2 , Miguel Ángel González-Barrio 3 , Matteo Jugovac 4 , Paolo Moras 4 , Igor Pis 5 , Federica Bondino 5 , Justin Pearson 6 , Richmond Shiwei Wang 6 , Ichiro Takeuchi 6 , Elliot J Fuller 7 , Alec A Talin 7 , Arantzazu Mascaraque 3 , Enrique G Michel 1, 2
ACS Applied Materials & Interfaces ( IF 8.3 ) Pub Date : 2023-07-19 , DOI: 10.1021/acsami.3c06147 Elena Salagre 1 , Pilar Segovia 1, 2 , Miguel Ángel González-Barrio 3 , Matteo Jugovac 4 , Paolo Moras 4 , Igor Pis 5 , Federica Bondino 5 , Justin Pearson 6 , Richmond Shiwei Wang 6 , Ichiro Takeuchi 6 , Elliot J Fuller 7 , Alec A Talin 7 , Arantzazu Mascaraque 3 , Enrique G Michel 1, 2
Affiliation
|
我们报告了一种基于离子溅射和退火循环的仅使用物理方法的LiCoO 2 (001) 阴极外延薄膜的新型脱锂工艺。优先进行锂溅射并随后进行退火，可产生锂摩尔分数在 0.5 < x < 1 范围内的表面层，其特征在于良好的结晶质量。这种脱锂过程可以明确地识别锂提取的影响，而不会产生化学副产物以及电解质与LiCoO 2表面相互作用引起的实验并发症。X射线光电子能谱（XPS）和X射线吸收光谱（XAS）的分析详细描述了脱锂过程以及O和Co原子在电荷补偿中的作用。我们观察到在去除 Li 后同时形成 Co 4+离子和位于 O 原子附近的空穴，而表面显示出 (2 × 1) 重建。这里描述的脱锂方法可以应用于其他晶体电池元件，并提供有关其特性的信息，而这些信息是其他方法难以获得的。
"点击查看英文标题和摘要"
更新日期：2023-07-19
"点击查看英文标题和摘要"
京公网安备 11010802027423号