Surface Modification Strategy Synthesized CsPbX3 Perovskite Quantum Dots with Excellent Stability and Optical Properties in Water
Advanced Functional Materials ( IF 18.5 ) Pub Date : 2023-02-14 , DOI: 10.1002/adfm.202300493
Shuo Song 1 , Yuchen Lv 1 , Bingqiang Cao 2 , Wenzhi Wang 1
Advanced Functional Materials ( IF 18.5 ) Pub Date : 2023-02-14 , DOI: 10.1002/adfm.202300493
Shuo Song 1 , Yuchen Lv 1 , Bingqiang Cao 2 , Wenzhi Wang 1
Affiliation
|
The poor stability of CsPbX3 (X = Cl, Br, I) perovskite quantum dots (PQDs) in polar solvents such as water, seriously hinders their practical application. Herein, 5-Bromovaleric acid (BVA) is used to replace oleic acid (OA), the most common surface ligand in CsPbX3 PQDs synthesis. Under the synergic action of oleylamine (OLA), CsPbX3 PQDs with high water stability can be synthesized directly in water. Because the carboxyl ligands provided by BVA, and the long chain amines provided by OLA formed hydrophobic shells on the surface of CsPbBr3 PQDs, the obtained CsPbBr3 PQDs still has high luminescence intensity and photoluminescence quantum yield after being dispersed in water for several days, and the luminescence peak is always maintained at 518 nm. In contrast, the luminescence intensity of CsPbBr3 PQDs synthesized with OA and OLA is <1% of the initial intensity after only 30 min. CsPbCl3 and CsPbI3 PQDs synthesized directly in water by this method also show high water stability. In this study, for the first time the synthesis method of CsPbX3 PQDs with high water stability using BVA/OLA as surface ligands is proposed, which provides an effective way to explore the synthesis of PQDs that can maintain stability in water.
中文翻译：
表面改性策略合成的 CsPbX3 钙钛矿量子点在水中具有优异的稳定性和光学性能
CsPbX 3 (X = Cl, Br, I)钙钛矿量子点（PQDs）在水等极性溶剂中的稳定性差，严重阻碍了它们的实际应用。在此，5-溴戊酸 (BVA) 用于替代油酸 (OA)，油酸是 CsPbX 3 PQD 合成中最常见的表面配体。在油胺（OLA）的协同作用下，可以直接在水中合成具有高水稳定性的CsPbX 3 PQD。由于BVA提供的羧基配体和OLA提供的长链胺在CsPbBr 3 PQDs表面形成疏水壳层，得到的CsPbBr 3PQDs在水中分散数天后仍具有较高的发光强度和光致发光量子产率，发光峰始终保持在518 nm。相比之下，仅 30 分钟后，用 OA 和 OLA 合成的 CsPbBr 3 PQD 的发光强度就小于初始强度的 1%。通过这种方法直接在水中合成的CsPbCl 3和CsPbI 3 PQDs也表现出很高的水稳定性。本研究首次提出了以BVA/OLA为表面配体的高水稳定性CsPbX 3 PQDs的合成方法，为探索在水中保持稳定性的PQDs的合成提供了有效途径。
更新日期：2023-02-14
中文翻译：
表面改性策略合成的 CsPbX3 钙钛矿量子点在水中具有优异的稳定性和光学性能
CsPbX 3 (X = Cl, Br, I)钙钛矿量子点（PQDs）在水等极性溶剂中的稳定性差，严重阻碍了它们的实际应用。在此，5-溴戊酸 (BVA) 用于替代油酸 (OA)，油酸是 CsPbX 3 PQD 合成中最常见的表面配体。在油胺（OLA）的协同作用下，可以直接在水中合成具有高水稳定性的CsPbX 3 PQD。由于BVA提供的羧基配体和OLA提供的长链胺在CsPbBr 3 PQDs表面形成疏水壳层，得到的CsPbBr 3PQDs在水中分散数天后仍具有较高的发光强度和光致发光量子产率，发光峰始终保持在518 nm。相比之下，仅 30 分钟后，用 OA 和 OLA 合成的 CsPbBr 3 PQD 的发光强度就小于初始强度的 1%。通过这种方法直接在水中合成的CsPbCl 3和CsPbI 3 PQDs也表现出很高的水稳定性。本研究首次提出了以BVA/OLA为表面配体的高水稳定性CsPbX 3 PQDs的合成方法，为探索在水中保持稳定性的PQDs的合成提供了有效途径。