用于高压锂离子电池的电解液聚合诱导阴极-电解液-相间
Advanced Energy Materials ( IF 24.4 ) Pub Date : 2021-09-12 , DOI: 10.1002/aenm.202101956 Jixiang Yang 1 , Xiang Liu 2 , Yian Wang 1 , Xinwei Zhou 3 , Lutao Weng 4 , Yuzi Liu 3 , Yang Ren 5 , Chen Zhao 2 , Mouad Dahbi 6 , Jones Alami 6 , Deia Abd Ei‐Hady 7 , Gui‐Liang Xu 2 , Khalil Amine 2, 8 , Minhua Shao 1
Advanced Energy Materials ( IF 24.4 ) Pub Date : 2021-09-12 , DOI: 10.1002/aenm.202101956 Jixiang Yang 1 , Xiang Liu 2 , Yian Wang 1 , Xinwei Zhou 3 , Lutao Weng 4 , Yuzi Liu 3 , Yang Ren 5 , Chen Zhao 2 , Mouad Dahbi 6 , Jones Alami 6 , Deia Abd Ei‐Hady 7 , Gui‐Liang Xu 2 , Khalil Amine 2, 8 , Minhua Shao 1
Affiliation
|
基于 LiNi x Co y Mn 1-xy O 2 (NCM) 正极材料的锂离子电池 (LIB)因其高能量密度、良好的倍率性能和相对较低的成本而被广泛商业化。然而，随着Ni含量的增加以进一步提高其能量密度，其循环稳定性急剧恶化，从而无法满足商业应用要求。人工阴极-电解质-界面（CEI）是解决这个问题的一种很有前途的方法。在这里，通过异丙醇铝 (AIP) 诱导的碳酸亚乙酯的原位聚合制造了坚固的 CEI。通过在商业电解液中添加 1 wt.% AIP，LiNi 0.8 Co的容量保持率0.1 Mn 0.1 O 2 ||Li 电池在 1 C 倍率下从 80.8% 显着增加到 97.8%，200 次循环后具有 176 mA hg -1的高度可逆容量。AIP 还可用作浆料制备过程中的添加剂，即使在 4.6 V 的高充电截止电压下，LiCoO 2 200 次循环后的可逆容量仍为 170 mA hg -1。原位形成的CEI层可以防止阴极开裂并减少不可逆相变。
"点击查看英文标题和摘要"
更新日期：2021-10-21
"点击查看英文标题和摘要"
京公网安备 11010802027423号