PLGA-PEG-PLGA are copolymers, able to form temperature-dependent hydrogels or sol dispersions at selective conditions. A general overview about the rheological characterization of their aqueous dispersions, focusing how the structural characteristics (e.g. molecular weight, PEG/PLGA ratio) affect their temperature-dependent behaviour, is presented. Different PLGA-PEG-PLGA were synthesized by varying the amount of lactide and glycolide and the amount and molecular weight of PEG. All polymers were characterised by gel-permeation chromatography and differential scanning calorimetry. Then, polymeric dispersions in water (15%-25% w/w) were analysed by oscillatory rheological measurements. At solid state, all copolymers are amorphous and the calculated glass transition temperatures were dependent on PEG/PLGA ratio. As regard aqueous dispersions, the temperature-dependent rheological behaviour named “partially thermogelling” has been described, in addition to the commonly reported thermogelling one. In these samples, the consistency increases over temperature without forming a three-dimensional network as for real hydrogels. All rheological characteristics can be explained according to the proposed categorization (thermogel, partial thermogel and sol dispersion).