纳米TiO2浆料
Titanium Paste |
Product Details |
Specifications |
Quantity |
Transparent Screen-printing Titanium Paste SIC-TiO2-T |
l Suit for screen-printing l Highly transparent film l ~3 μm layer after sintering at 500 °C for 30 minutes (325 mesh/cm screen)
|
Crystallization：Anatase Average Nanoparticle Size：20~30nm TiO2 Content：17~18%
|
10g |
50g |
|||
100g |
|||
500g |
|||
1kg |
|||
Scattering Screen-printing Titanium Paste SIC-TiO2-D |
l Mixed with large scattering particles l Suit for screen-printing; l Scattering and opaque white film l 3~4 μm layer after sintering at 500 °C for 30 minutes (325 mesh/cm screen) |
Crystallization：Anatase/Rutile Average Particle Size： 20~30nm(nanocrystal)/ 200~400nm(large scattering particles) TiO2 Content：17~18% |
10g |
50g |
|||
100g |
|||
500g |
|||
1kg |
|||
Blocking Screen-printing Titanium Paste SIC-TiO2-R |
l Suit for screen-printing; l Blocking and opaque white film l ~4 μm layer after sintering at 500 °C for 30 minutes (325 mesh/cm screen) |
Crystallization： Rutile Average Particle Size：200~400nm TiO2 Content：~20% |
10g |
50g |
|||
100g |
|||
500g |
|||
1kg |
高导电碳浆料
Carbon Pastes |
Product Details |
Specifications |
Quantity |
Low-temperature carbon paste |
l Suit for screen-printing l Suit for low-temperature process l Highly conductive film |
Composition: ≤ 20µm graphite particles, carbon black nanoparticles Carbon Content： ~30% Vehicle: solvent with low boiling point |
10g |
50g |
|||
100g |
|||
500g |
|||
1kg |
|||
Sintered carbon paste |
l Suit for screen-printing l Suit for high-temperature process l Highly conductive film |
Composition: ≤ 20µm graphite particles, carbon black nanoparticles Carbon Content： ~30% Vehicle: solvent with high boiling point |
10g |
50g |
|||
100g |
|||
500g |
|||
1kg |
敏化染料
Dye |
Molecular Structure |
CAS No. |
Remarks |
N719 |
|
207347-46-4 |
Absorption max = 522 - 530nm (DMF) Hydrophilic |
Z907 |
|
502693-09-6 |
Absorption max =518 - 526nm (DMF) Hydrophobic |
Z991 |
|
—— |
Absorption max =550 - 556nm (DMF) Hydrophobic |
TG6 |
|
—— |
Absorption max =545 - 550 nm (DMF) Hydrophobic |
C106 |
|
1152310-69-4 |
Absorption max =547 - 553 nm (DMF) Hydrophobic |